Wooden container and a process for manufacturing thereof

ABSTRACT

A wooden container formed by a wooden sheet is provided. The wooden container ( 1 ) is formed by a ply wood sheet comprising two wooden sheets chosen from a large number of wooden sheets, one being an inferior sheet ( 6   a ) including at least one spoiled portion and another one being a superior sheet ( 6   b ) including no such spoiled portion. The inferior and superior sheets are laid with each other and glued mutually. The container comprising a bottom wall ( 2 ) and a peripheral wall ( 3 ) is formed inside with the superior sheet ( 6   b ) and outside with the inferior sheet ( 6   a ). Adhesion film ( 9 ) is formed between contacted surfaces of the sheets by lignin oozed from wood content. Supplementary adhesion may be added if necessary.

FIELD OF THE INVENTION

The present invention relates to a wooden container such as tray and also to a process for manufacturing thereof wherein the container is formed by a plywood sheet comprising an inferior wooden sheet and a superior wooden sheet.

BACKGROUND OF THE INVENTION

It is known that a tray-like container for packing and selling food, fresh food such as fishes or vegetables for example, is formed and shaped by a foamed plastic sheet generally. The container is usually in white color, a film printed with a wood-grain pattern may be laminated on the plastic sheet in order to create a high grade appearance.

Since the plastic container has a problem of waste treatment, it is desirable to spread wooden containers widely as possible which can be incinerated. In addition, wooden containers are excellent in hygroscopicity etc., they fit packing wet food. For this reason, a wooden container formed by a wooden thin plate is already proposed in prior art.

A wooden container in prior art is formed by a single wooden plate which is heated and pressed by up-and-down dies to provide a bottom wall and a peripheral wall of the container. The wooden plates for manufacturing such containers are obtained by slicing wood pieces.

High-quality wood which has few damages such as cracks for example may provide good wooden plates for manufacturing containers. However, even high-quality wood may include knots so that a container formed by such a wooden plate as obtained by the high-quality wood may also include a knot, and the container leak moisture of wet food packed therein through the knot.

For this reason, a wooden plate having a knot cannot be used for manufacturing containers and must be discarded. It causes waste of resources.

From a viewpoint of using resources effectively, it is desirable to use not only high-quality wood but also low-quality wood obtained by trees which are produced when thinning out a forest. Usually, timbers obtained from such thinner trees are in low quality having many damaged portions as well as knots, they do not fit wood material for furniture and other wooden products, only limited uses are available, such as being used for a park bench for example, otherwise they are discarded.

It is desirable to use wooden plates obtained from thinner trees for manufacturing wooden containers. However, if the container is formed by such plate, knots as well as many damages, such as cracks, may be included so that moisture of wet food packed in the container may leak outside.

SUMMERY OF THE INVENTION

The inventor of the present invention found that it is certainly provided two kinds of wooden sheet by slicing a whole part of timber obtained from a good-quality tree. One is a small number of inferior sheets having spoiled portions such as knots or damages represented by cracks, and another one is a large number of superior sheets having no such spoiled portion.

On the contrary, when timber obtained from a thinner tree is sliced, many inferior sheets having spoiled portions such as knots and cracks and few superior sheets having no such spoiled portion are provided.

The inventor of the present invention studied how to use wood resources effectively without discarding inferior sheets and found it advantageous to provide a wooden container having a bottom wall and a peripheral wall, the container being formed by a plywood sheet comprising an inner ply of superior sheet and an outer ply of inferior sheet.

The inferior sheet includes a spoiled portion, such as knot and crack, but it is located in outside, it does not cause trouble in the function of container. Moisture of wet food packed in the container does not leak outside, since the inside of container is formed with the superior sheet having no spoiled portion.

Thereby, in comparison with prior art in which a container is formed by one single superior plate so that any inferior plates are to be discarded without being used, the present invention makes it possible to use effectively whole part of timber including spoiled portions without discarding any part of the timber.

According to the present invention, the total thickness (t) of the plywood sheet comprising the inferior and superior sheets may be designed as substantially same to the thickness (t) of one single plate of prior art container. It contributes to save resources, without increasing the amount of wood consumption per container as compared with prior art.

The present invention provides a wooden container made by a plywood sheet comprising an inferior wooden sheet having at least one spoiled portion and a superior wooden sheet having no such spoiled portion, said container being formed with a bottom wall and a peripheral wall by pressing said plywood sheet within up-and-down dies of a press apparatus wherein an inside of the container is formed by said superior wooden sheet and an outside of the container is formed by said inferior wooden sheet.

The present invention also provides a process for manufacturing a wooden container including a bottom wall and a peripheral wall comprising: a step of providing a large number of wooden sheets by slicing wooden pieces and forming a smooth surface and a fluffy rough surface on respective sides of each wooden sheet; a step of selecting a pair of wooden sheets, one being an inferior sheet including at least one spoiled portion and another one being a superior sheet including no such spoiled portion, and forming a plywood sheet by laying said two sheets together by contacting the respective fluffy rough surfaces; and a step of carrying out heating pressurization to said plywood sheet between male and female dies of a press apparatus under the state that said superior sheet faces the male die and said inferior sheet faces the female die whereby said wooden container having said bottom wall and said peripheral wall is formed while gluing said two sheets by oozing lignin and moisture from wood content to said rough surfaces.

The present invention further provides a process for manufacturing a wooden container including a bottom wall and a peripheral wall having a surrounding edge extending along an upper edge thereof in a shape of circular extending downward in cross section comprising: a step of providing a large number of wooden sheets by slicing wooden pieces and forming a smooth surface and a fluffy rough surface on respective sides of each wooden sheet; a step of selecting a pair of wooden sheets, one being an inferior sheet including at least one spoiled portion and another one being a superior sheet including no such spoiled portion, and forming a plywood sheet by laying said two sheets together by contacting the respective fluffy rough surfaces; a first forming step of producing an intermediate product by carrying out heating pressurization to said plywood sheet on its center region except its peripheral region between male and female dies of a press apparatus under the state that said superior sheet faces the male die and said inferior sheet faces the female die whereby said plywood sheet is formed with a bottom wall and a peripheral wall having an edge portion extending upwardly therefrom while gluing said two sheets by oozing lignin and moisture from wood content to said rough surfaces; and a second forming step of forming a finished product by carrying out further heating pressurization to said intermediate product by clamping entire part thereof whereby said bottom and peripheral walls are firmly pressed, said edge portion is formed with said surrounding edge, and the wooden container as the finished product is produced.

Preferably, the inferior and superior sheets are dried to reduce moisture in wood content before forming the plywood sheet. The reduced moisture of limited quantity may ooze to contacting surfaces of the inferior and superior sheets when heating pressurization is carried out to the plywood sheet.

According to the present invention, the contacting surfaces of the inferior and superior sheets are glued by lignin contained in wood content. However, supplementary adhesion may be added if necessary. For example, powder of starch may be applied by sprinkling on at least one of the rough surfaces of the inferior and superior sheets when joining mutually. The powder becomes paste with steam oozed from wood content when heating pressurization is carried out to the plywood sheet within the press apparatus so that the contacting surfaces of the inferior and superior sheets are glued mutually.

According to the present invention, the whole part of container is made wooden. The container can be incinerated, and the waste treatment is easy. The wooden container is excellent in hygroscopicity etc., it fits packing wet fresh food.

The wooden container is formed by a plywood sheet of a pair of wooden sheets selected from a large number of wooden sheets, one being an inferior sheet including a spoiled portion and another one being a superior sheet including no such spoiled portion. The plywood sheet is carried out with heating pressurization within a press apparatus so that the two sheets are glued together and the wooden container having a bottom wall and a peripheral wall is manufactured. Accordingly, such inferior wooden sheets are used effectively without discarding, it contributes to save resources.

According to the present invention, any parts to be discarded from wood are produced very few. Most part of the whole wood may be effectively used, and even wood obtained from thinner trees may also be used. The wooden container is manufactured at cheap cost by using such inferior sheet.

According to the present invention, the total thickness (t) of the plywood sheet comprising the inferior and superior sheets may be designed as substantially the same to the thickness (t) of one single plate of prior art container. It contributes to save resources, without increasing the amount of wood consumption per container as compared with prior art.

According to the present invention, the wooden container is formed with its inside by the superior sheet and its outside by the inferior sheet.

Although the inferior sheet includes the spoiled portions, such as knots or damages represented by cracks, it does not cause trouble in the function of container since the inferior sheet forms outside wall and not inside wall of the container. The inside wall of container is formed by the superior sheet, and moisture of wet fresh food packed in the container dose not leak outside.

According to the present invention, each of the inferior and superior sheets is formed with a smooth surface and a rough fluffy surface on respective sides. The plywood sheet is provided by laying such two sheets with the both rough surfaces being contacted mutually.

The plywood sheet is carried out with heating pressurization within the press apparatus. During the heating pressurization, lignin and moisture are oozed from wood content to the fluffy rough surfaces and form adhesion film by which the contacting surfaces of the inferior and superior sheets are glued mutually.

Any adhesives of organic synthetic resin are not used. It is sanitarily safe as a container for packing food, and moreover, it can contribute to environmental preservation, without generating harmful gas when incinerated. The surfaces of inside and outside of the container are made smooth, they are in good appearance, and touch is also good.

According to the present invention, a process for manufacturing a wooden container is offered wherein the peripheral wall is provided with a surrounding edge extending along an upper edge thereof in a shape of circular extending downward in cross section.

When a container packing food is wrapped by a film, the surrounding edge makes the wrapping operation easy. There are strong needs by users to use containers with such surrounding edge.

However, it is considered that, in case that a wooden container is manufactured by carrying out heating pressurization to a plywood sheet between male and female dies, the plywood sheet is formed at the same time with a bottom wall, a peripheral wall and a surrounding edge. In this case, the plywood sheet is pressed in such a direction as forming the bottom and peripheral walls while a peripheral edge of the peripheral wall being pulled in the same direction, and the peripheral edge is pressed at the same time in the opposite direction to form the surrounding edge. The probability of generating cracks at the peripheral edge becomes high.

To solve the problem of causing cracks, the present invention carries out two steps of forming, i.e., a first forming step and a second forming step.

The first forming step produces an intermediate product by carrying out heating pressurization to the plywood sheet within the press apparatus while gluing the inferior and superior sheets by oozing lignin and moisture from wood content to the rough surfaces contacted. The intermediate product is formed with a bottom wall and a peripheral wall having an edge portion extending upwardly therefrom. This means that the edge portion is not pressed.

The second forming step is subsequently carried out to produce a finished product by applying further heating pressurization to the intermediate product. The edge portion of the intermediate product is now pressed to be bent in circular extending downward. The finished product container having the surrounding edge is obtained and taken out the press apparatus.

Therefore, the probability of generating cracks at the peripheral edge becomes very low, and wooden containers having the surrounding edge are manufactured under good yields conditions.

In addition, the second forming step not only forms the surrounding edge, but clamps again the bottom and peripheral walls of the intermediate product. The bottom and peripheral walls are strongly clamped so that the plywood is stiffened firmly and improves intensity. In addition, even in case that the intermediate product formed by the first forming step includes distortion of a twist and the like in the bottom wall or the peripheral wall, such distortion is corrected by the second forming step.

According to the present invention, the inferior and superior sheets are decreased in moisture in wood content by drying in advance of carrying out heating pressurization to the plywood sheet.

According to the experiments by the inventor, the moisture remaining in the inferior and superior sheets is limited to substantially 10% to 20% in a preferred embodiment, and substantially 15% in the best mode, provided that moisture contained in natural wood is considered as 100%.

According to the knowledge acquired by the experiments, lignin in wood content will not be able to exude easily to the contacting surfaces of the inferior and superior sheets during heating pressurization to the plywood sheet, and it results poor adhesion, if moisture content is less than 10%.

On the contrary, if moisture content exceeds 20%, too much steam exudes during heating pressurization to dilute lignin, and it also results poor adhesion. It is found as the inventor's knowledge that a proper quantity of lignin can be made to ooze with a proper quantity of steam, and adhesion necessary for practical use of container is achieved, if moisture content is limited just over or below about 15%.

According to the present invention, even when the adhesion by lignin is insufficient, a wooden container in which the inner contacting surfaces of the plywood sheet are firmly glued is obtained.

As mentioned above, if the wooden sheets are dried so that moisture content may be made into about 10%-20%, good adhesion is achieved only by lignin. However, the quality control is not necessarily easy, and moreover, there is inconvenience that a drying process must be practiced.

To solve the problem of such inconvenience, powder of starch may be applied by sprinkling on at least one of the rough surfaces of the inferior and superior sheets. The powder may comprise flour for example, and a small quantity is sufficient for the application amount.

When the plywood sheet that the powder is applied between the inferior and superior sheets is carried out with heating pressurization within the press apparatus, lignin and steam are oozed from wood content, then the powder becomes paste with steam, and it spreads over and forms an uniform adhesion film to glue the contacting surfaces of the inferior and superior sheets.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1(A) to FIG. 1(C) show an embodiment of wooden container according to the present invention; FIG. 1(A) is a perspective view of the container, FIG. 1(B) is a longitudinal sectional view thereof, and FIG. 1(C) is an enlarged sectional view showing a broken part of plywood sheet.

FIG. 2(A) to FIG. 2(D) show a process of producing wooden sheets for manufacturing wooden containers according to the present invention: FIG. 2(A) is an explanatory view showing a slicing step of superior sheets, FIG. 2(B) is an explanatory view showing a slicing step of inferior sheets, FIG. 2(C) is an explanatory view showing an expansion step of the sheets, and FIG. 2(D) is an explanatory view showing a drying step of the sheets.

FIG. 3 is a sectional view showing an embodiment of press apparatus according to the present invention.

FIG. 4 is a sectional view showing the press apparatus wherein a first forming step to form an intermediate product is carried out.

FIG. 5 is a sectional view showing the press apparatus wherein a second forming step to form a finished product is carried out.

FIG. 6(A) and Fig. (B) are enlarged sectional views of the press apparatus in which an adjusting plate is used; FIG. 6(A) shows a forming step wherein a thin adjusting plate is used, and FIG. 6(B) shows a forming step wherein a thick adjusting plate is used.

DESCRIPTION OF PREFERRED EMBODIMENTS

Embodiments of the present invention are described in detail, referring to drawings.

An Embodiment of the Wooden Container

In FIG. 1, a wooden container 1 is illustrated as a tray, for example, having a bottom wall 2 and a peripheral wall 3, the tray may be shaped in either shallow or deep configuration. The tray has a surrounding edge 4 extending along the upper opening edge of peripheral wall 3 and also extending downward as circular in cross section. A bulge portion 5 may be formed by slightly lifting the center of bottom wall 2 so that moisture of wet food and like packed in the container may stagnate below the circumference of the bulge portion 5.

The wooden container 1 is formed by a plywood sheet 6 comprising an inferior sheet 6 a having spoiled portions such as knot or crack and a superior sheet 6 b having no such spoiled portion. The inferior sheet 6 a and the superior sheet 6 b are chosen from a large number of wooden sheets obtained by slicing a wooden piece. The plywood sheet 6 lays the inferior sheet 6 a and the superior sheet 6 b with each other, then the plywood sheet 6 is heated and pressed by up-and-down dies. The sheets 6 a and 6 b are glued mutually between the dies and formed in a shape of container 1 as mentioned above.

Accordingly, the whole part of container 1 is made wooden that can be incinerated easily so that no problem of waste treatment may be caused. Since the wooden container 1 is superior in hygroscopicity etc., it is suitable for packing fresh wet food.

As shown in FIGS. 1(B) and (C), the wooden container 1 is constructed such that an inner wall is formed with said superior sheet 6 b and an outside wall is formed with said inferior sheet 6 a.

As illustrated in FIG. 1(C), the inferior sheet 6 a includes spoiled portions 7, such as knots and cracks or the like. However, no trouble for packing function of the container is caused, since the inferior sheet 6 a is located in outside wall of the container.

On the other hand, the inside of container is formed with the superior sheet 6 b having no spoiled portion, and moisture of fresh food packed in the container does not leak outside.

The inferior sheet 6 a and the superior sheet 6 b, which constitute the plywood sheet 6, provide respective opposite sides with smooth surfaces but provide respective contact sides with rough surfaces 8 as shown in FIG. 1(C). Adhesion is carried out by adhesion film 9 formed between the contacted rough surfaces 8. The adhesion film 9 is made by lignin oozed from wood content to the rough surfaces 8 during the heating pressing process.

An Embodiment of a Process for Manufacturing the Container (Slicing Step)

As shown in FIG. 2(A), many superior sheets 6 b are formed by slicing a good-quality wooden piece 10 b. The sliced superior sheet 6 b is formed one side with a smooth surface and another side with a fluffy rough surface. A slice direction of the wood piece 10 b is set up so that grain may appear in the surfaces of superior sheet 6 b beautiful.

In the present invention, even low-quality wood 10 a containing spoiled portions 7, such as knot or crack, is used effectively without being discarded. That is, as shown in FIG. 2(B), many inferior sheets 6 a are formed by slicing a low-quality wooden piece 10 a. The sliced inferior sheet 6 a is formed one side with a smooth surface and another side with a fluffy rough surface. A slice direction of the wood piece 10 a is set up so that grain may appear in the surfaces of inferior sheet 6 a beautiful.

(Expansion Step)

The inferior sheet 6 a and the superior sheet 6 b may be distorted to an arch shape due to rotating cutters of slicing device. The distortion is corrected by inserting the sheets 6 a and 6 b through a pair of press rollers (not shown) of expansion device 11, as shown in FIG. 2(C).

(Drying Step)

Subsequently, the sheets 6 a and 6 b are decreased in moisture contained in wood content by drier 12, as shown in FIG. 2(D).

Under the condition that moisture contained in natural wood is considered as 100%, the sheets 6 a and 6 b are dried so that the moisture remains substantially 10% to 20%, preferably about 15%. In order to dry in short time, a heater is provided in the drier 12. The drier 12 may provide a zigzag-like passage through which the sheets 6 a and 6 b run in the predetermined distance. By controlling the heater and the running speed of the sheets 6 a, 6 b, it is possible to dry the sheets 6 a, 6 b remaining the limited moisture as mentioned above.

(First Forming Step)

A pair of inferior sheet 6 a and superior sheet 6 b is chosen from a large number of sheets obtained by those steps mentioned above. The sheets 6 a and 6 b are laid by contacting both rough surfaces 8 mutually to provide a plywood sheet 6.

The plywood sheet 6 is heated and pressed by a press apparatus 13 as shown in FIG. 3 to produce an intermediate processed container product 1 a (see FIG. 4).

When skipping the above mentioned drying step, or even when performing such drying step, powder of starch may be applied by sprinkling, if needed, on at least one of the rough surfaces 8 of the inferior sheet 6 a and the superior sheet 6 b. The powder may comprise flour for example, and a small quantity is sufficient for the application amount.

The press apparatus 13 forms, as a first forming step, an intermediate processed container product 1 a (herein called as “intermediate product”) which is provided with a bottom wall 2 a and a peripheral wall 3 a as shown in FIG. 4. However, an edge portion 4 a is extended upwardly from the peripheral wall 3 a. The center part of bottom wall 2 a is slightly lifted to provide a bulge portion 5 a preferably.

As shown in FIG. 3, the press apparatus 13 comprises a male die 14 shown as an upper die, and a female die 15 shown as a lower die. A driving source (not shown) is provided to open and close both dies 14 and 15.

The female die 15 has a concave 16 in a shape corresponding to the outside of said intermediate product 1 a, i.e., corresponding to the outside of the bottom wall 2 a including the bulge portion 5 a and the peripheral wall 3 a. An annular projection 17 is formed with the female die 15 at an opening edge of the concave 16. The annular projection 17 is in an arch-shape in cross section and extends outwardly from the concave 16.

The male die 14 comprises a main die 18 and a moving die 19. The moving die 19 is movable in forward and backward directions towards the female die 15 and is provided with a convex 20 in a shape corresponding to the inside of said intermediate product 1 a, i.e., corresponding to the inside of the bottom wall 2 a including the bulge portion 5 a and the peripheral wall 3 a.

The moving die 19 is guided by guide means 21 to move in forward and backward directions and is usually pushed by pushing means 22 having a spring 22 a so that the moving die 19 projects from the main die 18.

For manufacturing the intermediate product 1 a, the convex 20 of the moving die 19 forms the bottom wall 2 a and the peripheral wall 3 a at the same time, however, said edge portion 4 a is not pressed by the convex 20.

The main die 18 provides an annular groove 23 of which surface fits in a smooth manner to the peripheral edge of the convex 20 of the moving die 19 when the moving die 19 is moved fully backward.

The female die 15 has support means 24 projecting in the concave 16. The support means 24 comprises rods 24 a inserted through the female die 15 and springs 24 b pushing the rods 24 a towards the male die 14. The rods 24 a are movable in forward and backward directions and are usually pushed by the springs 24 b to advance into the concave 16 but stop at a position that each end of the rods 24 a comes at same level of the height of said annular projection 17.

An adjusting plate 25 is attached detachably to the female die 15 at the portion surrounding the annular projection 17, and positioning means 26 is provided at outside the adjusting plate 25. As shown in FIG. 3, the positioning means 26 is movable between a position close to the adjusting plate 25 as shown by a solid line in FIG. 3 and a position away from the female die 15 as shown by a chain line in FIG. 3.

Exhaust means 27 is provided on opposite faces of the male main die 18 and the female die 15. The exhaust means 27 is illustrated as being provided on the opposite faces, however, it may be formed by slot passages provided on at least one of the opposite faces, or by bore passages provided through at least one of the male and female dies.

As shown in FIG. 3, under the state that the press apparatus 13 is opened, the plywood sheet 6 is inserted between the up-and-down dies 14, 15 in such manner that the superior sheet 6 b faces the male die 14 and the inferior sheet 6 a faces the female die 15. As for the two sheets 6 a and 6 b comprising the plywood sheet 6, it is preferred to make the grains cross mutually.

When the plywood sheet 6 is put on the annular projection 17 of the female die 15, the positioning means 26 is positioned close to the projection 17 so that the periphery of the sheet 6 is restrained to be positioned at the predetermined position with respect to the female die 15. The center region of plywood sheet 6 is supported at the undersurface by support means 24, the sheet 6 does not bend downward.

Evacuating the positioning means 26 out of dies, as shown in FIG. 4, the dies 14 and 15 are closed and heating pressurization to the plywood sheet 6 is carried out to form the intermediate product 1 a.

When the male die 14 and the female die 15 are closed, the plywood sheet 6 is pressed by the convex 20 of the moving die 19 towards the concave 16 of the female die 15, and the plywood sheet 6 is deformed between the convex 20 and the concave 16, while the moving mold 19 being projected by pushing means 22.

As the moving die 19 gets closer to the female die 15, the moving die 19 is retreated in the main die 18 against the spring 22 a of the pushing means 22 while guided by the guide means 21. The convex 20 of the moving die 19 deforms the plywood sheet 6 and pushes it into the concave 16, while the undersurface of the sheet 6 is supported by the rods 24 a which retreat from the concave 16 against the spring 24 b.

The male die 14 and the female die 15 carry out the first forming step of the plywood sheet 6 where the dies 14 and 15 are not closed completely but are opened a little as shown in FIG. 4. The plywood sheet 6 is formed with the bottom wall 2 a and the peripheral wall 3 a to provide the intermediate product 1 a between the concave 16 and the convex 20. The moving die 19 is pushed by the spring 22 a of the pushing means 22 so that the plywood sheet 6 is clamped in the concave 6 and heating pressurization to the plywood sheet 6 is carried out.

In the first forming step, the annular groove 23 of the male main die 18 and the annular projection 17 of the female die 15 are apart mutually, therefore the edge portion 4 a of the intermediate product 1 a is not pressed. Thus, the first forming step forms the intermediate product 1 a with only the bottom wall 2 a and the peripheral wall 3. It does not cause the plywood sheet 6 any strong stress, and neither distortion nor a crack is produced.

The first forming step is carried out for several seconds, about 2 to 3 seconds for example, and the plywood sheet 6 is heated and pressed to form the intermediate product 1 a. The lignin and moisture in wood content of the plywood sheet 6 become steam and ooze to the rough surfaces 8 to glue together.

When powder of starch is applied to one of the rough surfaces as mentioned above, it becomes paste with steam, and it spreads over the rough surfaces 8 and glues together.

Steam generated during the first forming step is discharged out of the press apparatus 13 via exhaust means 27.

(Second Forming Step)

Subsequently, the press apparatus 13 is closed until the male die 14 and the female die 15 are brought in a complete clamp state to carry out a second forming step as shown in FIG. 5. Here, heating pressurization is performed again to the intermediate product 1 a, and a finished container product 1 is produced.

In the second forming step, the annular projection 17 of the female die 15 and the annular groove 23 of the male main die 18 are closed mutually, while the moving die 19 is retreated in the main die 18 so as to meet the peripheral edge of the convex 20 with the annular groove 23. The edge portion 4 a, which has not been pressed during the first forming step, is now heated and pressed to be shaped in a downward circle shape in cross section, thereby a surrounding edge 4 is formed.

In the second forming step, the intermediate product 1 a is clamped again while forming the surrounding edge 4. The bottom wall 2 a and the peripheral wall 3 a are firmly clamped stronger than the clamping operation in the first forming step. Therefore, the plywood comprising the finished container product 1 is stiffened firmly, and its intensity is improved. In addition, even in case that the intermediate product 1 a obtained by the first forming step includes distortion of a twist and the like in the bottom wall 2 a or the peripheral wall 3 a, such distortion is corrected by the second forming step.

A potential problem may be included in the second forming step that a crack is produced depending on the wood quality, when pressing the edge portion 4 a of the intermediate product 1 a to form the surrounding edge 4 of the finished container product 1. Such a crack has the tendency to be easy to generate if the upheaval of surrounding edge 4 becomes remarkable, in other words, the curvature radius of surrounding edge 4 becomes small.

For this reason, the press apparatus 13 provides the female die 15 with the adjusting plate 25 at outside portion near the periphery of annular projection 17. It is preferred that plural plates having different thicknesses are prepared to be selectively used, such as a first adjusting plate 25 a of comparatively small thickness T1 (2 mm in thickness for example) as shown in FIG. 6(A), and a second adjusting plate 25 b of comparatively large thickness T2 (3 mm in thickness for example). Each adjusting plate 25 forms an annular frame like configuration surrounding the outside of annular projection 17 and is attached on the female die 15 detachably.

The adjusting plate 25 may be removed when the second forming step is carried out. In case that no adjusting plate is attached, the surrounding edge 4 formed by the edge portion 4 a of the intermediate product 1 a becomes highest with respect to its height H.

If it seems that the surrounding edge 4 breaks in that condition, the first adjusting plate 25 a of small thickness T1 is attached as shown in FIG. 6(A), and the second forming step is carried out. Thereby, the problem of causing cracks may be solved since the surrounding edge 4 to be formed by the edge portion 4 a is made its height H1 lower than the case where the adjusting plate 25 a is not provided.

If it further seems that the surrounding edge 4 still breaks even the first adjusting plate 25 a attached, it is replaced with the second adjusting plate 25 b of large thickness T2 (namely, T2>T1) as shown in FIG. 6(B), and the second forming step is carried out. The problem of causing cracks will be solved since the surrounding edge 4 to be formed by the edge portion 4 a is made its height H2 further lower than the case where the first adjusting plate 25 a is attached (namely, H2<H1).

Although two or more kinds of adjusting plates 25 a and 25 b which have different thicknesses may be provided for selective use as mentioned above, plural adjusting plates of the same thickness may be also used to achieve adjusting of the height H by piling up the plates.

Another Embodiment of the Process

The foregoing embodiment which performs two steps of the first forming step and the second forming step corresponds to the invention defined in claim 3. It is not always necessary for the invention to perform two forming steps according to claim 2.

In case that a wooden container having no surrounding edge 4 is manufactured for example, the container may be formed by pressing a plywood sheet 6 only by one forming step of the press apparatus 13. 

1. A wooden container comprising a plywood sheet (6) which comprises an inferior wooden sheet (6 a) having at least one spoiled portion (7) and a superior wooden sheet (6 b) having no such spoiled portion, said container being formed with a bottom wall (2) and a peripheral wall (3) by pressing said plywood sheet (6) within up-and-down dies of a press apparatus, wherein an inside of the container is formed by said superior wooden sheet (6 b) and an outside of the container is formed by said inferior wooden sheet (6 a).
 2. A process for manufacturing a wooden container including a bottom wall (2) and a peripheral wall (3) comprising: a step of providing a large number of wooden sheets by slicing wooden pieces and forming a smooth surface and a fluffy rough surface (8) on respective sides of each wooden sheet; a step of selecting a pair of wooden sheets, one being an inferior sheet (6 a) including at least one spoiled portion (7) and another one being a superior sheet (6 b) including no such spoiled portion, and forming a plywood sheet (6) by laying said two sheets (6 a, 6 b) together by contacting the respective fluffy rough surfaces (8); and a step of carrying out heating pressurization to said plywood sheet (6) between male and female dies of a press apparatus under the state that said superior sheet (6 b) faces the male die and said inferior sheet (6 a) faces the female die whereby said wooden container having said bottom wall (2) and said peripheral wall (3) is formed while gluing said two sheets (6 a, 6 b) by oozing lignin and moisture from wood content to said rough surfaces (8).
 3. A process for manufacturing a wooden container including a bottom wall (2) and a peripheral wall (3) having a surrounding edge (4) extending along an upper edge thereof in a shape of circular extending downward in cross section comprising: a step of providing a large number of wooden sheets by slicing wooden pieces and forming a smooth surface and a fluffy rough surface (8) on respective sides of each wooden sheet; a step of selecting a pair of wooden sheets, one being an inferior sheet (6 a) including at least one spoiled portion (7) and another one being a superior sheet (6 b) including no such spoiled portion, and forming a plywood sheet (6) by laying said two sheets (6 a, 6 b) together by contacting the respective fluffy rough surfaces (8); a first forming step of producing an intermediate product (1 a) by carrying out heating pressurization to said plywood sheet (6) on its center region except its peripheral region between male and female dies of a press apparatus under the state that said superior sheet (6 b) faces the male die and said inferior sheet (6 a) faces the female die whereby said plywood sheet (6) is formed with a bottom wall (2 a) and a peripheral wall (3 a) having an edge portion (4 a) extending upwardly therefrom while gluing said two sheets (6 a, 6 b) by oozing lignin and moisture from wood content to said rough surfaces (8); and a second forming step of forming a finished product (1) by carrying out further heating pressurization to said intermediate product (1 a) by clamping entire part thereof whereby said bottom and peripheral walls (2 a, 3 a) are firmly pressed, said edge portion (4 a) is formed with said surrounding edge (4), thereby the wooden container as the finished product formed with said bottom wall (2), said peripheral wall (3) and said surrounding edge (4) is produced.
 4. A process for manufacturing a wooden container according to claim 2 wherein said inferior and superior sheets (6 a, 6 b) are dried to reduce moisture in wood content in advance of forming the plywood sheet (6), and said reduced moisture of limited quantity is oozed together with lignin form wood content to contacting surfaces of the inferior and superior sheets (6 a, 6 b) when heating pressurization is carried out to the plywood sheet (6), thereby said contacting surfaces are glued mutually.
 5. A process for manufacturing a wooden container according to claim 3 wherein said inferior and superior sheets (6 a, 6 b) are dried to reduce moisture in wood content in advance of forming the plywood sheet (6), and said reduced moisture of limited quantity is oozed together with lignin form wood content to contacting surfaces of the inferior and superior sheets (6 a, 6 b) when heating pressurization is carried out to the plywood sheet (6), thereby said contacting surfaces are glued mutually.
 6. A process for manufacturing a wooden container according to claim 2, wherein powder of starch is applied on at least one of the rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) when joining mutually, and said powder becomes paste with steam oozed from wood content when heating pressurization is carried out to the plywood sheet (6) within the press apparatus so that said rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) are glued mutually.
 7. A process for manufacturing a wooden container according to claim 3, wherein powder of starch is applied on at least one of the rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) when joining mutually, and said powder becomes paste with steam oozed from wood content when heating pressurization is carried out to the plywood sheet (6) within the press apparatus so that said rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) are glued mutually
 8. A process for manufacturing a wooden container according to claim 4, wherein powder of starch is applied on at least one of the rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) when joining mutually, and said powder becomes paste with steam oozed from wood content when heating pressurization is carried out to the plywood sheet (6) within the press apparatus so that said rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) are glued mutually
 9. A process for manufacturing a wooden container according to claim 5, wherein powder of starch is applied on at least one of the rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) when joining mutually, and said powder becomes paste with steam oozed from wood content when heating pressurization is carried out to the plywood sheet (6) within the press apparatus so that said rough surfaces (8) of the inferior and superior sheets (6 a, 6 b) are glued mutually 